2000×2000 Motor Test Platform

The testing platform is an important member of the cast iron platform family.
As a fundamental inspection tool in industrial production, the material selection and performance characteristics of cast iron testing platforms directly affect measurement accuracy and service life. Cast iron testing platforms are typically made of high-strength cast iron (HT200/HT300) or alloy cast iron as the primary materials. Both materials offer significant advantages in hardness, wear resistance, and stability, meeting the requirements of different precision grades and working conditions.
I. Main Material Types of Cast Iron Testing Platforms
1. High-Strength Gray Cast Iron (HT200/HT300)
This is a commonly used material for cast iron testing platforms, with a carbon content ranging between 2.8-3.6%. HT200 has a hardness of HB170-240 and a tensile strength of 200 MPa, while HT300 can achieve a tensile strength of 300 MPa with even higher hardness. Through proper casting processes and heat treatment, these materials form a uniform pearlite matrix with flake graphite distribution, ensuring both excellent damping performance and sufficient rigidity. For example, as mentioned in sources, the density of HT200 cast iron is approximately 7.2 g/cm³, and it has a low thermal expansion coefficient (11×10⁻⁶/°C), making it suitable for maintaining dimensional stability in environments with significant temperature variations.
2. Alloy Cast Iron
By adding alloying elements such as chromium, molybdenum, and copper to ordinary gray cast iron, the material's wear resistance and deformation resistance can be significantly improved. For instance, adding copper refines the graphite flakes and enhances the corrosion resistance of the cast iron, while chromium increases the hardness to above HB220, making it suitable for high-precision (Grade 00 and above) platforms. Although these materials are more expensive, their service life is extended by 30-50% compared to ordinary gray cast iron.
3. Ductile Cast Iron (QT500-7)
In a few special working conditions, ductile cast iron is used. Its graphite exists in a spherical structure, with a tensile strength of up to 500 MPa and an elongation of 7%. It combines the damping properties of cast iron with mechanical properties close to those of steel. However, due to high processing difficulty and cost, it is mostly used for heavy-duty or customized testing platforms.
II. Analysis of Core Performance Characteristics
1. Stability and Damping Performance
The internal graphite structure of cast iron materials can absorb mechanical vibrations, with a damping coefficient ranging from 0.02 to 0.06 (gray cast iron outperforms ductile cast iron in this regard). Experimental data from a 163 NetEase article show that the vibration decay time of an HT250 cast iron platform is 40% shorter than that of a steel platform, which is crucial for measurement accuracy. Additionally, the low thermal expansion特性 of cast iron ensures that the length change per meter does not exceed 8 μm in an environment of 20°C ± 5°C.
2. Wear Resistance and Hardness
The addition of alloying elements directly affects surface hardness. After special quenching, the surface hardness of cast iron can reach above HRC50, with wear resistance being only one-third that of ordinary cast iron. The working surface of the platform typically requires scraping treatment, with a contact point density of ≥25 points/25 mm² (Grade 00 standard), ensuring that precision is maintained even after long-term use.